Two-Component Solvent-Free Primer Coating Epoxy Resin Flooring Paint

• Customization: Available
• Appearance: Liquid
• Level: Primer
• Model NO.: FLD088
• Drying Method: Air Drying
• Certification: ISO14001, CCC, RoHS, ISO9001
• Substrate: Ceramic
• Components: Solvent
• Formation Mechanism: Conversion Type
• Place of Origin: Wuhan China
• Application: Mainly Used as a Sealing Coating on Cement Surface
• Complied Standardsrs: Complies with Jt/T 722-2008, It/T733-2008
• Features: Good Permeability and Sealing Performance
• Theoretical Coating Rate: 0.13kg/Square Meter
• Milxing Ratio: Base/Hardener=25/5
• Film Thickness: Dry:20-40microns/Coat Wet:40-80microns/Coat
• Flash Point: 27ºC
• Surface Drying: 8 Hours (25°c)
• Fully Cured: 24 Hours (25°c)
• Gloss: High Gloss
• Transport Package: Barrel
• Specification: 20 liter container holds 20 kg
• Trademark: FLDC
• Origin: Wuhan China
• HS Code: 3206421000
• Production Capacity: 100000

Product Description

Product Description

Two-Component Solvent-Free Primer Coating Epoxy Resin Flooring Paint

Overview: Solvent-free epoxy sealing primer is a two-component coating that uses epoxy resin as the main film-forming material and is mixed with an amine curing agent.

Key Features:

• Excellent Permeability and Sealing Resistance: Provides a robust barrier against contaminants.
• Superior Adhesion: Ensures strong bonding with subsequent coatings like epoxy and polyurethane paints.
• Alkali and Water Resistance: Protects surfaces from alkali and water damage.
• Water and Salt Water Resistance: Offers additional protection in moist or marine environments.
• Environmentally Friendly: VOC-free, reducing environmental impact.
• Quartz Powder Compatibility: Can be mixed with quartz powder for intermediate coatings or caulking.
• Application Flexibility: Used as a sealing primer on cement-based surfaces and as a mid-coat with quartz sand.

Applications: Ideal for sealing primer applications on cement-based surfaces. Also suitable for use with quartz sand as a mid-coat or for caulking purposes.

Technical Specifications:

Attribute	Description
Color	Transparent, slightly yellow.
Volume solid content	≥98%
Drying Time	Surface dry ≤6h, Hard dry ≤24h (at 25ºC)
Specific Gravity	150g-200g/square meter
Flash Point	38ºC

Construction Parameters:

1. Curing Time: New cement base surfaces must be cured for more than 28 days.
2. Surface Preparation: Mechanically polish cement to roughen, absorb floating dust, and ensure cleanliness.
3. Environmental Conditions: Avoid construction when ground moisture is below 5%, air humidity exceeds 85%, or temperature is below 5ºC.
4. Usage Time: Use the paint within half an hour of preparation to prevent gel waste.
5. Dilution: For use as a middle coating with sand, epoxy diluent can be added if viscosity is too high; diluent amount should not exceed 80% of the total.
6. Reaction Speed: Faster reaction at higher temperatures, shortening operation time.
7. Application Method: Scraping or rolling.

Packaging:

• Component A: 20L barrel, 24kg/backet.
• Component B: 4L square can, 4kg/can.

Company Profile

FAQ

1.What is a solvent-free epoxy sealing primer?
A solvent-free epoxy sealing primer is a coating that provides a sealant layer without the use of solvents, reducing VOC emissions.

2.How does HDDD-502 improve adhesion to subsequent coatings?
HDDD-502 features superior adhesion properties, ensuring a strong bond with coatings like epoxy and polyurethane paints.

3.What are the environmental benefits of using HDDD-502?
Being solvent-free, HDDD-502 reduces VOC emissions, contributing to a more environmentally friendly coating process.

4.Can HDDD-502 be used in areas exposed to water and salt water?
Yes, HDDD-502 offers excellent water and salt water resistance, making it suitable for use in moist or marine environments.

5.What is the drying time for HDDD-502 at 25ºC?
The surface drying time is ≤6 hours, and hard drying time is ≤24 hours at 25ºC.

6.What is the recommended application method for HDDD-502?
HDDD-502 can be applied by scraping or rolling, providing flexibility in application techniques.

7.Can HDDD-502 be used with quartz sand as a mid-coat?
Yes, HDDD-502 can be mixed with quartz sand for use as a mid-coat or for caulking, enhancing its versatility.

8.How should HDDD-502 be stored to maintain its quality?
Store HDDD-502 in a cool, dry place away from direct sunlight and heat sources. The effective storage period is one year.

9.What safety precautions should be taken when using HDDD-502?
Wear protective gear, maintain ventilation, and avoid contact with skin and eyes. In case of contact, rinse thoroughly.

10.How does the addition of quartz powder affect HDDD-502?
Adding quartz powder can enhance the wear resistance and durability of the coating, making it suitable for intermediate coatings or caulking.